Abstract

Verbatim from NASA NTRS. Not paraphrased, not summarized.

The damage tolerance of composites was investigated. Results show that severe degradation in material strength may occur due to impact damage and that reduced strain allowables should be considered to compensate for possible impact damage. The mechanisms of failure involved in impact so that local damage will be reduced and arrest of propagating fracture initiated at impact locations are examined. Compression strength reductions for damage due to impact by a 1.27 cm diameter spherical projectile in thick laminates representative of wing skin panels are presented. Also discussed are the results of concepts recently evaluated to improve damage tolerance. These concepts range from improvements at the materials level to advanced structural configurations designed to arrest or limit the growth of propagating fractures. The results indicate that substantial improvements in the damage tolerance of graphite-epoxy composite structures can be achieved through the proper combination of materials and structural design.

Author

• Rhodes, M. D. NASA Langley Research Center